| Specification |
Color: White;
Diameter: 3 mm;
Material: Alumina;
Surface Finish: Polished;
Usage: Chemical;
|
Material: Alumina;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-120mm;
Isostatic Pressing: 25-90mm;
Application: Architectural, Medical, Refractory, Ball Mill;
Type: Ceramic Ball;
Grain Size: 0.5-120mm;
Purity: 92;
|
Material: Alumina;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-120mm;
Isostatic Pressing: 25-90mm;
Application: Architectural, Medical, Refractory, Polishing Machine;
Type: Ceramic Ball;
Grain Size: 0.5-120mm;
Purity: 92;
|
Material: Alumina;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
Application: Architectural, Refractory, Polishing Machine;
Type: Ceramic Ball;
Grain Size: 0.5-120mm;
Purity: 92;
|
Color: White;
Diameter: 0.5-120mm;
Material: Aluminum;
Usage: Ball Mill;
Ai2o3: 95%;
Sio2: 2.80%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-120mm;
Isostatic Pressing: 25-90mm;
Standard: Other;
Application: Metallurgical Machinery, Ball Mill, Mining Machine;
Type: Wear Resistant Ceramic;
|