| Specification |
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: ≥48%;
Apparent Porosity: ≤23%;
|
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Al2O3: 45% ;60%;70%;
Fe2o3: 0.8-1.6%Max;
TiO2: 2-2.8%;
K2o: 0.1-1.5%;
Density: 2.4-2.8g/cm3;
Mullite Phase: 80-90;
Refracotry temperature: 1790-2200;
Grade: M45;M60;M70;
Type: Refractory Material;
Material: Mullite;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Single Gross Weight: 1015.000kg;
Cao Content %: 0.01%;
Size: Customizable;
Refractoriness (Degree): Common1580< Refractoriness< 1770;
Cro Content %): 0.1%~0.3%;
Bulk Density: 2.35g/cm3;
Material: Alumina Block;
Sic Content %): 1.2%~1.4%;
Cold Crushing Strength: 30MPa;
Sio2 Content %): 94-96%;
Refractory Under Load @0.2MPa: 1640-1660c;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Single Gross Weight: 1015.000kg;
Cao Content %: 0.01%;
Size: Customizable;
Refractoriness (Degree): Common1580< Refractoriness< 1770;
Cro Content %): 0.1%~0.3%;
Bulk Density: 2.35g/cm3;
Material: Alumina Block;
Sic Content %): 1.2%~1.4%;
Cold Crushing Strength: 30MPa;
Sio2 Content %): 94-96%;
Refractory Under Load @0.2MPa: 1640-1660c;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Corrosion Resistant;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Usage: Refractoy;
MGO Content (%: 0.01%;
Single Gross Weight: 1015.000kg;
Refractoriness (Degree): 1770<Refractoriness<2000;
Sio2 Content %: 20%~30%;
Cro Content %): 0.1~0.3%;
Single Package Size: 100X100X110.Cm;
Bulk Density: 2.75~3.1g/cm3;
Material: Alumina Block;
Sic Content (%): 1.2-1.4%;
Al203 Content %): 60%-80%;
Cold Crushing Strength: 70-90MPa;
Cao Content %): 0.34%;
Application: Industrial Furnaces;
|